MT-OA110G is a polyester based powder coating, formulated without TGIC.
| ケミカルタイプ | Polyester TGIC-free |
| 外観 | スムースマット |
| 粒径 | Suitable for electrostatic spray |
| 比重 | 1.53-1.63g /cm³ |
| フィルムの厚さ | 75〜100ミクロン |
| カバレッジ | 7.8 ㎡/kg @ 75 microns |
| Storage | Dry cool conditions below 25°C (open boxes must be resealed) |
| 賞味期限 | 12か月間 |
| Stoving schedule (object temperature) | 10℃で200分 |
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| 基板 | Gold Seal polished steel |
| 前処理 | Lightweight Zinc phosphate |
| フィルムの厚さ | 70〜80ミクロン |
| Stoving Schedule | 10℃で200分 |
| test | 結果 | |
| 柔軟性 | ISO6860 | 5 mm |
| Erichsen cupping | ISO1520 | 6 mm |
| 接着 | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | 30±5％ |
| Hardness(Buchholz) | ISO2815 | 8-125 |
| Reflectance Class | EN 16268 | A |
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA110G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
MT-OA110G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566