MT-Active is a powder coating primer, totally free from Zinc. It is designed to give enhanced corrosion protection of mild steel and is an epoxy-polyester primer including active anticorrosive pigments. The addition of these pigments provides a steel passivation effect to protect the substrate enhancing the performance when compared to other non-active systems.
| ケミカルタイプ | Thermosetting epoxy-polyester |
| 外観 | スムーズ |
| Gloss level (60°) | 50-60ユニット |
| 色圏 | グレー |
| Recommended Film Thickness (µm) | 60 - 80μm |
| 密度（グラム/ cm3） | 1.65～1.70g/cm³ |
| Application | 静電気 |
| Storage | Under dry, cool (≤ 30°C) conditions |
| 賞味期限 | At least 12 months from production date |
| Flexibility (Cylindrical Mandrel) | ASTM D522-93A | Pass 3 mm (Primer) Pass 10 mm (System) |
| 接着 | ASTM D3359-97 (2mm crosshatch) | Class 0 (Primer) Class 0 (System) |
| エリクセンカッピング | ASTM643-84 | Pass 5 mm (Primer) Pass 4 mm (System) |
| 影響 | ASTM D2794 | Pass 0.4 kg·m (Primer) Pass 0.3 kg·m (System) |
Surface preparation depends upon the metal, the type of surface, its conditions and the required performance.
| 基板 | Mechanical pretreatment | Chemical pretreatment |
| 軟鋼 | Grit Blasting Sa 2.5 in accordance with ISO NF EN 8501-1. Roughness: Rz 42 84 µm / Ra 6-12 µm | Degreasing & phosphating (or equivalent) followed by passivation, DW rinsing and drying. |
| 鋳鋼 | ||
| Electro Zinc steel | Sweep blasting with a maximum zinc layer thickness reduction of 5 to 10 µm depending on the initial zinc thickness | |
| Hot dip galvanized stee | Degreasing & phosphating / chromating followed by passivation. | |
| flame/electrical deposition) | Grit Blasting Sa 3 in accordance with ISO NF EN 8501-1. Roughness: Rz 42 84 µm / Ra 6-12 µm | 禁止された |
For help with solutions customized to your business needs, contact Export Director now.