MT-A1230 series covers a wide range of powder coatings specifically designed to meet the extreme demands of automotive components. Demanding environments require high performance protection. MT-A1230 will enhance and protect automotive parts with excellent chemical, corrosion and chip resistance as well as the right aesthetic appearance exactly where it's needed.
| Chemical Type | Epoxy-Polyester |
| Area of usage | Automotive mechatronic components and systems |
| Related Specifications | Brose 587000-110 / Group 2 |
| Appearance | Smooth |
| Gloss level (60°) | 52 ± 4 GU |
| Colour | Black |
| Recommended Film Thickness (µm) | 80 ± 40 µm |
| Density (g/cm3) | 1.46 ± 0.03 |
| Gel time (at 200 °C) | 36 - 54sec |
|
Coverage at 60 µ Coverage at 80 µ |
93.0 g/m2 or 10.8 m2/kg 124.0 g/m2 or 8.1 m2/kg |
| Application | Corona Only - Electrostatic (30 – 100 kV) |
| Storage | Under dry, cool (<25°C) conditions |
| Shelf life | At least 12 months from production date |
|
Curing schedule (at object temperature) |
10 minutes at 180°C (please see curing window) |
|
Adhesion |
DIN EN ISO 2409 | Gt 0 |
| Erichsen cupping | DIN EN ISO 1520 | ≥ 5 mm |
| Buchholz indentation | DIN EN ISO 2815 | > 80 |
| Cylindrical mandrel | DIN EN ISO 1519 | ≤ 6 mm |
MT-A1230 powders can be applied by manual or automatic electrostatic spray equipment. It is recommended that for consistent application and appearance product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Steel surfaces to be coated must be clean and free from grease. For maximum protection it is essential to pre-treat components prior to the application of MT-A1230. Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance.
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566