MT-300 is a series of polyester resin based thermo-setting powder coatings formulated using TGIC. The pigments used in the MT-300 series restrict the field of application of this powder coatings class to interior uses. MT-300 is designed for interior decoration such as, metal furniture, shop fittings, shelves, light fittings.
| Tüüpiline väärtus | |
| Keemiline tüüp | Polüester – TGIC |
| Tihedus | 1.2–1.9 g/cm³, olenevalt värvist ja efektist |
| Soovitatav kile paksus | 60–90 µm |
| Säilitusaeg | 12 kuud alla 30 °C |
| Ladustamistingimused | (open boxes must be resealed) Dry, cool conditions |
| Kõvenemise ajakava | 12–24 minutit 180 °C juures 8–16 minutit 200 °C juures 4–10 minutit 210 °C juures (objekti temperatuuril) |
Tsingitud teras vajab pinna ettevalmistamist kas mitmeastmelise eeltöötluse abil, kasutades kas tsinkfosfaadi või -kromaadi konversiooni või kontrollitud pühkimispritsimist. Sõltuvalt tsingimise tüübist võib olla vajalik degaseerimine või mullitamisvastaste lisandite kasutamine – järgige eeltöötluse tarnija protseduurilisi juhiseid. Raudfosfaat ja eriti tsinkfosfaatimine mustade metallide puhul parandab korrosioonikindlust. Alumiiniumist aluspinnad võivad vajada kromaadi konversioonikatet.
Powders can be applied by manual or automatic electrostatic spray equipment. A good protection is linked with the recommended film thickness. Bonded products have better application properties than blended products (more stable) but attention should still be paid to line settings in order to avoid “marble effect” and changes in aspect after recycling. Different substrates (aluminium, steel, galvanized steel…), use of primer, and big changes in film thickness may give a different aspect. Products with different codes should not be mixed even if same colour and gloss. It is recommended that for consistent application and appearance product be fluidized during application. MT-300 powder coatings can be applied by corona electrostatic or tribostatic equipment. However, the aspect obtained by tribo static equipment may vary when compared to electrostatic application and/or our color card.
Toote tegelik toimivus sõltub toote kasutamise asjaoludest. Katsed on tehtud laboritingimustes, kasutades järgmisi rakendusomadusi, ja need on ainult soovituslikud.
| Eeltöötlus | Tsinkfosfaat |
| Substraat | Polished steel |
| Kõvenemise ajakava | 12 minutit temperatuuril 200 °C (objekti temperatuur) |
| Filmi paksus | 60–70 µm |
| Tüüpiline väärtus | Meetod/standard | |
| kleepumine | Klass 0 | ISO 2409 (2 mm ristviirutus) |
| Erichseni kuputamine | Läbi 5 mm | ISO 1520 |
| Paindlikkus | Läbi 5 mm | ISO 1519 |
| Kõvadus | Läbitud – aluspinnale tungimist ei toimunud | ISO 1518-1 (2000g) |
| Löögitugevus | ≥30 kg.cm | ISO 6272-2 (d/r) |
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566