Product Introduction:
This is a thermosetting epoxy-modified heavy-duty anti-corrosion powder coating specifically designed for epoxy-coated reinforcing steel. The product uses imported two-step special epoxy resins, functional epoxy resins, and dedicated anti-corrosion curing agents. It features excellent reactivity, strong adhesion, good toughness and flexibility, and superior resistance to chemicals, solvents, cathodic disbondment, and impact. The formulation has been tested and proven effective by authoritative departments.
Ominaisuudet:
Erinomainen tarttuvuus alustaan.
Tiivis, yhtenäinen, kirkas pinnoite, jolla on alhainen läpäisevyys ja minimaaliset neulanreiät.
Erinomainen katodisen irtoamisen kestävyys ja korkea sähköeristys.
High bond strength with concrete and strong grip.
Good toughness, does not crack when bent.
Alhainen sulamislämpötila, korkea reaktiivisuus, korkea kovettumisnopeus ja hyvät mekaaniset ominaisuudet.
Monipuolinen ja pieni jauheenkulutus.
Vähentää tai poistaa säikeiden muodostumisen pulverimaalausprosessin aikana.
Jauhemaalauksen suorituskykyparametrit
| erä | Laatuindikaattori | Testausmenetelmä |
|---|---|---|
| Esiintyminen | Yhtenäinen väri, ei paakkuja | Silmämääräinen tarkastus |
| Väri | Asiakkaan vaatimusten mukaan | ----- |
| Tiheys (g / cm³) | 1.2-1.5 | GB / T 4472 |
| Keskimääräinen hiukkaskoko | 30µm-50µm | Laserhiukkaskoon analysaattori |
| Haihtuva pitoisuus (%) | ≤ 0.6 | GB / T 6554 |
| Magneettisen aineen pitoisuus (%) | ≤ 0.002 | GB / T 2482-86 |
| Kovettumisaika (s) | 230°C ≤ 60s | GB / T 6554 |
Kovettunut jauhemaalausominaisuudet
| Ei. | Testi Tuote | Tekninen indikaattori | Testausmenetelmä |
|---|---|---|---|
| 1 | Esiintyminen | Smooth, continuous, no bubbles, cracks, or pinholes | Silmämääräinen tarkastus |
| 2 | Cathodic Disbondment | ≤ 2 mm | GB / T 25826-2010 |
| Jatkuvuus | No holes, gaps, cracks, or visible defects | GB / T 25826-2010 | |
| 3 | Flexibility (40mm) | No visible cracks, breaks, or coating detachment | GB / T 25826-2010 |
| 4 | Siteen vahvuus | Coating bond strength not less than 85% of uncoated steel | GB 50152 |
| 5 | Vaikutusvoima | No coating fragmentation | GB / T 25826-2010 |
| 6 | Chloride Permeability | < 1×10⁻⁴ M | GB / T 25826-2010 |
| 7 | Kemiallinen resistanssi | No softening, bubbling, good adhesion, no pinholes, no pitting | GB / T 25826-2010 |
| 8 | Hiomakestävyys | ≤ 100 mg | GB / T 1768-1979 |
| 9 | Suolasumutesti (800 h) | ≤ 3 mm | GB / T 25826-2010 |
Vaatimustenmukaisuusstandardit: JG 3042-1997; GB/T 25826-2010
Sovellus Fields:
Bridges, ports, airports, buildings, basements, high-speed railways, and other infrastructure projects.
Hakuprosessi:
Sähköstaattinen ruiskutus.
Varotoimet:
The reinforcing steel surface should be free of oxide scale, revealing the metal’s original color; the surface roughness should meet the standard, ideally 50-70 mm; the rust removal grade should reach Sa2 1/2 level (GB/T 8923), with no chloride residues. Preheating temperature should be controlled between 220-245°C.
Tuotetta tulee säilyttää hyvin ilmastoidussa, kuivassa sisätilassa alle 27 °C:n lämpötilassa, poissa lämmönlähteistä, syövyttävistä kemikaaleista ja kemiallisista liuottimista sekä suojattuna voimakkaalta valolta. Pinoamiskorkeus ei saa ylittää neljää kerrosta. Vältä pitkäaikaista painetta ja varmista, että pakkauslaatikko on suljettu paakkuuntumisen ja kosteuden estämiseksi, jotka voivat vaikuttaa fluidisaatiotehoon.
Due to the high reactivity of this product, the recommended storage period is within 3 months at 27°C. If used beyond the storage period, the performance should be verified in advance.
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566