MT-100 is a series epoxy based powder coatings that exhibit excellent corrosion protection and chemical resistance when applied over a properly prepared metal substrate. MT-100 is designed for interior application only. MT-100 powders are available in gloss, satin, matt and texture finishes in a wide range of colors.
| Typyske wearde | |
| Gemyske Type | Epoksy |
| Befolkingstichtens | 1.2 – 1.9 g/cm³, ôfhinklik fan kleur en effekt |
| Oanrikkemandearre filmdikte | 60 - 90 µm |
| Hâld it libben | 12 moannen |
| Opslach Betingsten | Under droege, koele (≤ 25 °C) omstannichheden (iepene doazen moatte opnij fersegele wurde) |
| Curing skema | 15-20 minuten op 180 °C 9-12 minuten op 190 °C 5-7 minuten op 200 °C |
Aluminiumkomponinten moatte in folsleine mearfaze chromaatkonverzjecoating krije of in geskikte chromefrije foarbehanneling of in geskikte foar-anodisaasje om it substraat skjin te meitsjen en te kondisjonearjen. Detaillearre advys moat yntsjinne wurde by de leveransier fan 'e foarbehanneling. Izerfosfaat en benammen sinkfosfatering fan ferrometalen ferbetteret de korrosjebestriding. Aluminiumsubstraten kinne in chromaatkonverzjecoating fereaskje.
Powders can be applied by manual or automatic electrostatic spray equipment. Applicators and fabricators are advised to use a single batch for parts that will be assembled together. Differences are more likely with special effect powders. Bonded products have better application properties than blended products (more stable) but attention should still be paid to line settings in order to avoid “marble effect” and changes in aspect after recycling. Different substrates (aluminium, steel, galvanized steel…), use of primer, and big changes in film thickness may give a different aspect. Products with different codes should not be mixed even if same colour and gloss. It is recommended that for consistent application and appearance product be fluidized during application.
| Bewurkingsmetoade | Tribo, Electrostatic |
| Recycling | Unused powder can be reclaimed using suitable equipment and recycled through the coating system, but a minimum of 70% virgin powder should be used. |
De werklike produktprestaasjes sille ôfhingje fan 'e omstannichheden wêryn't it produkt brûkt wurdt. De resultaten binne basearre op meganyske en gemyske testen dy't (útsein as oars oanjûn) útfierd binne ûnder laboratoariumomstannichheden en allinich as begelieding jûn wurde.
| Pre-behanneling | Sinkfosfaat |
| Substrate | Gepolijst stiel |
| Curing skema | 5 min by 200 °C (objekttemperatuer) |
| Film dikte | 60 - 70 µm |
| Typyske wearde | Metoade/standert | |
| adhesion | Klasse 0 | ISO 2409 (2 mm krúsarsearring) |
| Erichsen cupping | Trochgean 5 mm | ISO 1520 |
| fleksibiliteit | Trochgean 5 mm | ISO 1519 |
| hurdens | Trochgean - gjin penetraasje nei substraat | ISO 1518-1 (2000g) |
| Impact resistance | Trochjaan 2.5 Joules efterút & direkt (20 yn lb) | ISO 6272-2 (d/r) |
Whilst maintaining the general protective and anti-corrosive properties of powder coatings, aluminum and copper/bronze metallic finishes, when submitted to the listed tests, may rapidly show a loss of metallic aspect. The results shown are based on tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for advice only, actual performance depends upon the circumstances under which the product is used.
| Typyske wearde | Metoade/standert | |
| Gemyske wjerstân | Excellent resistance to acid, alkalis, oils and chemicals at room temperatures. | |
| Sâlt spray test | Pass, no corrosion creep more than 3 mm from scribe, 500 h | ISO 9227 |
| Typyske wearde | Metoade/standert | |
| Temperatur | Pass – no blistering or loss of gloss, 1000 h | ISO 6270-2 CH (Constant humidity) |
| Exterior durability | Some chalking and loss of gloss after 3-6 months continuous outdoor exposure. Protective properties retained. Not recommended for outdoor applications. |
| Surface tarieding | Damaged areas must be clean and free of grease or rust. Dry-sand the area with 600 grade paper down to the substrate. The area must be completely free of dust and cleaned with a non-aggressive solvent before proceeding. Any damage of the coating system must be repaired as soon as possible. |
| Oanfraach | For repairs a PU (2K or 1K) liquid paint is recommended. |
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566