MT-OA110G is a polyester based powder coating, formulated without TGIC.
| 화학물질 종류 | Polyester TGIC-free |
| 외관 | 부드러운 매트 |
| 입자 크기 | Suitable for electrostatic spray |
| 비중 | 1.53-1.63g / cm³ |
| 도막 두께 | 75 – 100 마이크론 |
| 적용 범위 | 7.8 ㎡/kg @ 75 microns |
| 스토리지 | Dry cool conditions below 25°C (open boxes must be resealed) |
| 유통 기한 | 12 개월 |
| Stoving schedule (object temperature) | 10°C에서 200분 |
The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| 기판 | Gold Seal polished steel |
| 전처리 | Lightweight Zinc phosphate |
| 도막 두께 | 70 – 80 마이크론 |
| Stoving Schedule | 10°C에서 200분 |
| test | 결과 | |
| 유연성 | ISO6860 | 5mm |
| Erichsen cupping | ISO1520 | 6mm |
| 부착 | ISO2409 | 100% |
| Impact (dir/rev) | ISO 6272 | 30/30 kgcm |
| Gloss(@60°） | ISO 2813 | 30 ± 5 % |
| Hardness(Buchholz) | ISO2815 | 8-125 |
| Reflectance Class | DIN EN 16268 | A |
Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-OA110G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.
MT-OA110G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
For help with solutions customized to your business needs, contact Export Director now.
Export Director
With 20+ years of experience and We firmly believe that product quality is the basis of cooperation.
Send Inquiry
TEl
+86-21-6420 0566