(FBE) Single Layer Epoxy Anti-Corrosion Powder Coating

Surface Finish Options Overview

mankhwala Introduction:
This product is carefully formulated using epoxy resin and functional curing agents. It features high reactivity, strong adhesion, high cross-link density, and excellent resistance to chemicals, solvents, cathodic disbondment, as well as superior flexibility and impact resistance.

Kugwiritsa Ntchito Zogulitsa:
Suitable for anti-corrosion of oil and gas transmission pipelines, municipal water supply, drainage, sewage, circulating water, chemical industry, and can also serve as a base layer for anti-corrosion in thermal insulation and submarine cable applications.

Zambiri Zamalonda:

Excellent adhesion to the substrate.Good leveling of the coating surface with moderate gloss.Strong resistance to permeation and corrosion.High surface hardness and dense coating, good resistance to plant root penetration.Excellent high-temperature cathodic disbondment resistance.Low melting temperature, high reactivity, high curing completion rate.

Ufa Magwiridwe:

Powder Coating Performance Parameters

Chiyeso	luso mfundo	ndemanga
Maonekedwe	Uniform color, no lumps	Kuyendera kowoneka
mtundu	Monga momwe kasitomala amafuna	Mitundu yamitundu yosiyanasiyana
Kachulukidwe (g/cm³)	1.3-1.5	GB / T 4472
Kugawa Kwakukulu kwa Particle	Residuals ≤3.0 at 150um, ≤0.2 at 250um	GB / T 6554
Non-volatile Content (%)	≤99.4	GB / T 6554-1986
Magnetic Substance Content (%)	≤0.002	GB / T 2482-1986
Gellation Time at 180°C (s)	.100s	GB / T 6554-1986
Gellation Time at 200°C (s)	.60s	GB / T 6554-1986
Gellation Time at 230°C (s)	.30s	GB / T 6554-1986

Cured Powder Coating Performance Parameters

Chiyeso	luso mfundo	ndemanga
Maonekedwe	Smooth, uniform color, no bubbles, no cracks, allows slight orange peel	Kuyendera kowoneka
Adhesion (Grade)	1-3	SY/T 0315-2005
Negative Electrode at 24h (mm)	≤6.5	SY/T 0315-2005
Negative Electrode at 28d (mm)	≤8	SY/T 0315-2005
Cross-sectional Crack Rate	1-4	SY/T 0315-2005
Coating Surface Porosity Rate	1-4	SY/T 0315-2005
Bending Resistance (3°)	Palibe ming'alu	SY/T 0315-2005
Kukaniza kwa Voliyumu	≤1*10¹³	GB / T 1410
Electric Strength (MV/m)	≥30	GB / T 1408.1
Impact Resistance (1.5J at -30°)	No leakage points	SY/T 0315-2005
Kukaniza Chemical	oyenerera	SY/T 0315-2005
Wear Resistance (Abrasion Method)	≤3	SY/T 0315-2005
Salt Spray Test (1000h)	Coating shows no change	GB / T 1771-1991

Execution Standard:
SY/T 0315-2005 “Technical Specification for Single Layer Fusion Bonded Epoxy Powder Coating on Steel Pipes”

Kuchiritsa Zinthu:

katundu	mfundo	ndemanga
kutentha	200-230°C for 3-1.5 minutes	Medium-frequency heating recommended

Magawo Ntchito:

chizindikiro	mfundo	zolemba
Zida Zogwiritsidwa Ntchito	Frictional charging spray, corona electrostatic spray
Kutayika kwa Mafilimu	250-450um	Adjustable according to workpiece requirements

Nthawi Yosungira:

The product can be stored for 6 months in dry conditions below 30°C.The used coating must be re-sealed immediately to prevent moisture absorption affecting performance.Packaging: 20kg paper boxes lined with plastic bags.

Health and Safety:

The product is non-toxic and non-flammable, but follow GB15607-1995 coating operation safety regulations when using.

CHENJEZO:

Do not mix different types of powders.Not recommended for outdoor use; fading and chalking may occur with long-term outdoor exposure.The steel pipe surface should be free of oil and moisture, with surface treatment quality reaching Sa21/2 level (GB/T8923), anchor pattern depth should be 40-100um, and the surface should be cleaned of dust and abrasives.Preheating: The temperature should be controlled between 180-230°C.